Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

POSPÍŠILOVÁ, S.; OBRTLÍK, K.; JULIŠ, M.; PODRÁBSKÝ, T.

Original Title

Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

English Title

Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

Type

Peer-reviewed article not indexed in WoS or Scopus

Original Abstract

This paper is focused on the study of initiation and growth of fatigue cracks in IN713LC with Al protective coating and without coating. Microstructure characteristics and microhardness of Al coating are documented. Fatigue crack initiation and fatigue crack growth mechanisms were identified. The crack propagation rates were obtained based on striation spacing in fracture surfaces.

English abstract

This paper is focused on the study of initiation and growth of fatigue cracks in IN713LC with Al protective coating and without coating. Microstructure characteristics and microhardness of Al coating are documented. Fatigue crack initiation and fatigue crack growth mechanisms were identified. The crack propagation rates were obtained based on striation spacing in fracture surfaces.

Keywords

low cycle fatigue, IN713LC, aluminide coating, crack initiation, crack propagation rate

Key words in English

low cycle fatigue, IN713LC, aluminide coating, crack initiation, crack propagation rate

Authors

POSPÍŠILOVÁ, S.; OBRTLÍK, K.; JULIŠ, M.; PODRÁBSKÝ, T.

RIV year

2012

Released

19.07.2011

Publisher

Chemické listy

Location

Novotného lávka 5 Praha 1

ISBN

0009-2770

Periodical

CHEMICKE LISTY

Volume

105

Number

S

State

Czech Republic

Pages from

840

Pages to

841

Pages count

2

Full text in the Digital Library

BibTex

@article{BUT72857,
  author="Simona {Hutařová} and Karel {Obrtlík} and Martin {Juliš} and Tomáš {Podrábský}",
  title="Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC",
  journal="CHEMICKE LISTY",
  year="2011",
  volume="105",
  number="S",
  pages="840--841",
  issn="0009-2770"
}