Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition

WASSERBAUER, J.; BUCHTÍK, M.; TKACZ, J.; FINTOVÁ, S.; MINDA, J.; DOSKOČIL, L.

Originální název

Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition

Anglický název

Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition

Druh

Článek WoS

Originální abstrakt

The corrosion behavior of duplex Ni-P coatings deposited on AZ91 magnesium alloy was studied. The electroless deposition process of duplex Ni-P coating consisted in the preparation of low-phosphorus Ni-P coating (5.7 wt.% of P), which served as a bond coating and high-phosphorus Ni-P coating (11.5 wt.% of P) deposited on it. The duplex Ni-P coatings with the thickness of 25, 50, 75 and 100 µm were deposited on AZ91 magnesium alloy. The electrochemical corrosion behavior of coated AZ91 magnesium alloy was investigated by electrochemical impedance spectroscopy and potentiodynamic polarization method in 0.1 M NaCl. Obtained results showed a significant improvement in the corrosion resistance of coated specimens when compared to uncoated AZ91 magnesium alloy. From the results of the immersion tests in 3.5 wt.% NaCl, 10% solution of HCl and NaOH and 5% neutral salt spray, a noticeable increase in the corrosion resistance with the increasing thickness of the Ni-P coating was observed.

Anglický abstrakt

The corrosion behavior of duplex Ni-P coatings deposited on AZ91 magnesium alloy was studied. The electroless deposition process of duplex Ni-P coating consisted in the preparation of low-phosphorus Ni-P coating (5.7 wt.% of P), which served as a bond coating and high-phosphorus Ni-P coating (11.5 wt.% of P) deposited on it. The duplex Ni-P coatings with the thickness of 25, 50, 75 and 100 µm were deposited on AZ91 magnesium alloy. The electrochemical corrosion behavior of coated AZ91 magnesium alloy was investigated by electrochemical impedance spectroscopy and potentiodynamic polarization method in 0.1 M NaCl. Obtained results showed a significant improvement in the corrosion resistance of coated specimens when compared to uncoated AZ91 magnesium alloy. From the results of the immersion tests in 3.5 wt.% NaCl, 10% solution of HCl and NaOH and 5% neutral salt spray, a noticeable increase in the corrosion resistance with the increasing thickness of the Ni-P coating was observed.

Klíčová slova

Ni-P coating; AZ91 magnesium alloy; electroless deposition; corrosion; electrochemical test

Klíčová slova v angličtině

Ni-P coating; AZ91 magnesium alloy; electroless deposition; corrosion; electrochemical test

Autoři

WASSERBAUER, J.; BUCHTÍK, M.; TKACZ, J.; FINTOVÁ, S.; MINDA, J.; DOSKOČIL, L.

Rok RIV

2021

Vydáno

17.03.2020

Nakladatel

MDPI

Místo

Basel, Switzerland

ISSN

1996-1944

Periodikum

Materials

Svazek

13

Číslo

6

Stát

Švýcarská konfederace

Strany od

1

Strany do

17

Strany počet

17

URL

https://www.mdpi.com/1996-1944/13/6/1357/htm

Plný text v Digitální knihovně

http://hdl.handle.net/11012/188109

BibTex

@article{BUT162737,
  author="Jaromír {Wasserbauer} and Martin {Buchtík} and Jakub {Tkacz} and Stanislava {Fintová} and Jozef {Minda} and Leoš {Doskočil}",
  title="Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition",
  journal="Materials",
  year="2020",
  volume="13",
  number="6",
  pages="1--17",
  doi="10.3390/ma13061357",
  issn="1996-1944",
  url="https://www.mdpi.com/1996-1944/13/6/1357/htm"
}

Dokumenty

materials-13-01357