THE IMPORTANCE OF CURRENT MODE ON THE PROPERTIES OF PEO COATINGS DEPOSITED ON THE SURFACE OF POWDER METALLURGY-PRODUCED MG SUBSTRATE

THE IMPORTANCE OF CURRENT MODE ON THE PROPERTIES OF PEO COATINGS DEPOSITED ON THE SURFACE OF POWDER METALLURGY-PRODUCED MG SUBSTRATE

Stať ve sborníku v databázi WoS či Scopus

Plasma electrolytic oxidation (PEO) technique is a process of surface treatment of light metallic materials such as magnesium alloy, to produce coatings increasing the corrosion resistance. In this work, the effect of direct or alternating current deposition mode on the structure and corrosion behavior of PEO coatings on Mg substrates prepared by powder metallurgy (PM) was studied. It was observed that during the deposition process of PEO coatings, the varying of current mode between alternating current (AC) and direct current (DC) led to significantly different surface modifications and coatings properties. In the case of DC PEO coatings, significantly higher thickness was achieved than in the case of AC PEO coatings. On the other hand, AC PEO coatings achieved smaller pore sizes compared to the DC PEO coatings. Considering the denser and less porous structure of AC PEO coating, significantly better electrochemical properties were observed using potentiodynamic measurements in Hank's solution. Compared to the uncoated PM Mg substrate, there was an order of magnitude decrease in the icorr of PEO-coated Mg substrate. In the case of DC PEO coatings, the i(corr) value was determined to be 8.3 mu A.cm(-2), and in the case of AC PEO even 3.4 mu A.cm(-2).

Plasma electrolytic oxidation (PEO) technique is a process of surface treatment of light metallic materials such as magnesium alloy, to produce coatings increasing the corrosion resistance. In this work, the effect of direct or alternating current deposition mode on the structure and corrosion behavior of PEO coatings on Mg substrates prepared by powder metallurgy (PM) was studied. It was observed that during the deposition process of PEO coatings, the varying of current mode between alternating current (AC) and direct current (DC) led to significantly different surface modifications and coatings properties. In the case of DC PEO coatings, significantly higher thickness was achieved than in the case of AC PEO coatings. On the other hand, AC PEO coatings achieved smaller pore sizes compared to the DC PEO coatings. Considering the denser and less porous structure of AC PEO coating, significantly better electrochemical properties were observed using potentiodynamic measurements in Hank's solution. Compared to the uncoated PM Mg substrate, there was an order of magnitude decrease in the icorr of PEO-coated Mg substrate. In the case of DC PEO coatings, the i(corr) value was determined to be 8.3 mu A.cm(-2), and in the case of AC PEO even 3.4 mu A.cm(-2).

Magnesium, powder metallurgy, PEO coating, corrosion, Hank's solution

Magnesium, powder metallurgy, PEO coating, corrosion, Hank's solution

BUCHTÍK, M.; SOMANOVA, P.; KOBZINKOVÁ, E.; BŘEZINA, M.; DOSKOČIL, L.

2026

01.01.2024

Tanger Ltd

SLEZSKA

978-80-88365-21-1

METAL-Conference Proceedings

346

351

6