Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys

MACA, K., CIHLÁŘ, J.

Originální název

Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys

Anglický název

Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys

Druh

Kapitola, resp. kapitoly v odborné knize

Originální abstrakt

The structure of interaction interface after contact of molten nickel alloys Ni20Cr and Ni20Cr5Ti with the single crystal alumina of defined orientation at the temperature range from 1773K to 1973K for 8 and 16 hours and under pressure of argon atmosphere 0.12MPa was investigated by means of SEM, microananlysis and XRD analysis.

Anglický abstrakt

The structure of interaction interface after contact of molten nickel alloys Ni20Cr and Ni20Cr5Ti with the single crystal alumina of defined orientation at the temperature range from 1773K to 1973K for 8 and 16 hours and under pressure of argon atmosphere 0.12MPa was investigated by means of SEM, microananlysis and XRD analysis.

Klíčová slova v angličtině

alimina, nickel alloys, interaction

Autoři

MACA, K., CIHLÁŘ, J.

Vydáno

01.01.1994

Nakladatel

The Federation of European Materials Societies

Místo

Lausanne, Švýcarsko

Kniha

Junior Euromat 94

Strany od

9

Strany počet

1

BibTex

@inbook{BUT51736,
  author="Karel {Maca} and Jaroslav {Cihlář}",
  title="Mechanism of Interaction between Single Crystal Alumina and Molten Ni-alloys",
  booktitle="Junior Euromat 94",
  year="1994",
  publisher="The Federation of European Materials Societies",
  address="Lausanne, Švýcarsko",
  pages="1"
}