Plasmachemical Removal of Corrosion Layers from Brass
KRČMA, F.; MAZÁNKOVÁ, V.; SÁZAVSKÁ, V.; ŘÁDKOVÁ, L.
Originální název
Plasmachemical Removal of Corrosion Layers from Brass
Anglický název
Plasmachemical Removal of Corrosion Layers from Brass
Druh
Stať ve sborníku v databázi WoS či Scopus
Originální abstrakt
Influence of RF low-pressure hydrogen plasma on corroded brass samples was investigated. OH radicals formed during this process were measured by optical emission spectroscopy; simultaneously, sample temperature was measured by a thermocouple. The value of integral intensity of OH radicals represented quantitative ablation of oxygen from a corrosion layer. Sample temperature was an important indicator of sample protection against metallographic changes. It was proved that both hydrogen atom reduction and thermal decomposition were employed in the removal process.
Anglický abstrakt
Influence of RF low-pressure hydrogen plasma on corroded brass samples was investigated. OH radicals formed during this process were measured by optical emission spectroscopy; simultaneously, sample temperature was measured by a thermocouple. The value of integral intensity of OH radicals represented quantitative ablation of oxygen from a corrosion layer. Sample temperature was an important indicator of sample protection against metallographic changes. It was proved that both hydrogen atom reduction and thermal decomposition were employed in the removal process.
Klíčová slova
RF low-pressure hydrogen plasma, brass corrosion, atomic hydrogen
Klíčová slova v angličtině
RF low-pressure hydrogen plasma, brass corrosion, atomic hydrogen
Autoři
KRČMA, F.; MAZÁNKOVÁ, V.; SÁZAVSKÁ, V.; ŘÁDKOVÁ, L.
Rok RIV
2013
Vydáno
10.07.2012
Nakladatel
EPS
Místo
Lisbon
ISBN
2-914771-74-6
Kniha
Europhysics Conference Abstracts
Strany od
P2.3.31
Strany do
P2.3.32
Strany počet
2
Plný text v Digitální knihovně